    Comparison of fiber reinforcing methods of composite resin: Aflexural strength and stereo microscopy study
    (Wiley, 2023) Cengiz, Seda; Bağış, Bora; Külünk, Şafak; Velioğlu, Neslin; Sağlam, Gaye
    This study aimed to compare the effect of fiber reinforcing methods on the flexural strength and failure modes of indirect composite resins. Based on the reinforcement methods, the bar specimens (3 x 3 x 25 mm) were divided into five groups (n = 20). Glass or polyethylene fibers were used for reinforcement of indirect composite resins. Fibers were either light polymerized and mixed with indirect composite resin or mixed with indirect composite resin after resin application and polymerized together. Indirect composite resin without fiber reinforcement was used as control. All five types of specimens were stored in distilled water at 37 & DEG;C for 24 h. Half of the specimens were additionally thermocycled. Then the specimens were tested in a three-point bending test. Failure types were examined and categorized by using stereo microscope. The data were analyzed using two-way ANOVA and Tukey HSD test. Flexural strength was found to be significantly higher for fiber-reinforced indirect resin composites than control. However, the fiber-reinforced groups did not present any significant difference. Analysis revealed aging does not affect the flexure strength of fiber reinforcement of indirect composite resin. The study concluded that the flexure strength of indirect composite resins was improved with fiber reinforcement. Different fiber reinforcement methods demonstrated similar effects on the flexure strength of indirect composite resin. Reinforcement with glass or polyethylene fibers presented the potential to improve the mechanical properties of indirect composite resins. Research Highlights Flexural strength of indirect composite resins are affected by the reinforcement of composites with glass or polyethylene fibers. Aging with thermocycling has no effect on the flexural strength of the indirect composite resins, however can cause catastrophic failures in material.